PHYSICAL

METHOD

CONDITION

UNIT

VALUE

Melt Index

ASTM D1238

190¡É/2.16kg

g/10min

0.05

Melting Temperature

DSC

10¡É/min

¡É

133

Density

ASTM D792

23¡É

g/cm³

0.953

CHARATERISTICS

METHOD

CONDITION

UNIT

VALUE

Tensile Strength at Yield

ASTM D882

MD

kg/cm²
MPa
psi

360
35.5
5119.2

ASTM D882

TD

kg/cm²
MPa
psi

380
37.5
5403.6

Tensile Strength at Break

ASTM D882

MD

kg/cm²
MPa
psi

590
58.2
8389.8

Tensile Strength at Yield

ASTM D882

TD

kg/cm²
MPa
psi

610
60.2
8674.2

Elongation at Break

ASTM D882

MD

%

640

ASTM D882

TD

%

540

Tear Strength

ASTM D1922

MD

g

100

ASTM D1922

TD

g

22

Dart Impact Resistance

ASTM D1709

-

g

240

Film Thickness

-

-

µm

30